Triantafyllopoulos, Clin Orthop Relat Res 2016 - Otto Aufranc Award: Large Heads Do Not Increase Damage at the Head-Neck Taper of Metal-On-Polyethylene Total Hip Arthroplasties - Article Summary

Otto Aufranc Award: Large Heads Do Not Increase Damage at the Head-Neck Taper of Metal-On-Polyethylene Total Hip Arthroplasties

Triantafyllopoulos, Wright, et al.·Clin Orthop Relat Res·2016·99 citations·Retrospective cohort

Background

Fretting and corrosion at head-neck junctions of total hip arthroplasties (THAs) have been associated with adverse local tissue reactions in patients with both metal-on-polyethylene (MoP) and metal-on-metal (MoM) prostheses. Femoral head size contributes to the severity of fretting and corrosion in large-diameter MoM THAs, but its impact on such damage in MoP THAs remains unknown.

Purpose

(1) Is femoral head size associated with increased fretting or corrosion at the head-neck junction in MoP total hips? (2) Is duration of implantation associated with increased fretting or corrosion?

Methods

The severity of fretting/corrosion on surfaces of head tapers and stem trunnions was visually examined in 154 MoP THAs retrieved as part of 3282 revision surgeries performed at our institution between January 1, 2007, and December 31, 2013.
Fretting and corrosion damage were subjectively graded by two independent observers on a 1 to 4 scale, and their relations to head size, alloy combinations, taper/trunnion design, length of implantation (LOI), and location were investigated.
Differences in scores never exceeded one grade, and this occurred in only 17% of examined implants.
With the available implants, the study provided 88% power to detect differences of 0.5 in fretting or corrosion scores in these analyses.

Results

Fretting and corrosion of the tapers and the trunnions were not affected by head size (p = 0.247, p = 0.471, p = 0.837, and p = 0.868, respectively), although taper/trunnion design affected taper fretting (p = 0.005) and corrosion (p = 0.0031) and trunnion fretting (p = 0.0028).
Head taper fretting (observed in 73% of heads) increased with LOI, but head taper corrosion (noted in 93% of heads) was not affected.
Trunnion fretting (observed in 86% of stems) was more severe in mixed-alloy combinations and with increased LOI and was more severe proximally.
Trunnion corrosion (noted in 72% of stems) was also location-dependent with greater corrosion distally.

Conclusions

Fretting and corrosion are regular occurrences in MoP THAs, but neither damage type was related to femoral head size. Conversely, taper design, LOI, and alloy combination affected the severity of both fretting and corrosion.

Clinical Relevance: Although it has been suggested that trunnion corrosion seen in MoP bearings is a function of larger diameter heads, our data suggest that larger femoral heads may be used for increased damage at the modular junction of MoP THAs.